Influence of porcelain firing and cementation on the marginal adaptation of metal-ceramic restorations prepared by different methods
Özet
Statement of problem. Marginal adaptation plays an important role in the survival of metal ceramic restorations. Porcelain firings and cementation may affect the adaptation of restorations. Moreover, conventional casting procedures and casting imperfections may cause deteriorations in the marginal adaptation of metal-ceramic restorations. Purpose. The purpose of this in vitro study was to compare the marginal adaptation after fabrication of the framework, porcelain application, and cementation of metal-ceramic restorations prepared by using the conventional lost-wax technique, milling, direct metal laser sintering (DMLS), and LaserCUSING, a direct process powder-bed system. Alterations in the marginal adaptation of the metal frameworks during the fabrication stages and the precision of fabrication methods were evaluated. Material and methods. Forty-eight metal dies simulating prepared premolar and molar abutment teeth were fabricated to investigate marginal adaptation. They were divided into 4 groups (n=12) according to the fabrication method used (group C serving as the control group: lost-wax method; group M: milling method; group LS: DMLS method; group DP: direct process powder-bed method). Sixty marginal discrepancy measurements were recorded separately on each abutment tooth after fabrication of the framework, porcelain application, and cementation by using a stereomicroscope. Thereafter, each group was divided into 3 subgroups according to the measurements recorded in each fabrication stage: subgroup F (framework), subgroup P (porcelain application), and subgroup C (cementation). Data were statistically analyzed with univariate analysis of variance (followed by 1-way ANOVA and Tamhane T2 test (alpha=.05). Results. The lowest marginal discrepancy values were observed in restorations prepared by using the direct process powder-bed method, and this was significantly different (P<.001) from the other methods. The highest marginal discrepancy values were recorded after the cementation procedure in all groups. Conclusions. The results showed that the direct process powder-bed method is quite successful in terms of marginal adaptation. The marginal discrepancy increased after porcelain application and cementation.