Influence of different staining beverages on color stability, surface roughness and microhardness of silorane and methacrylate-based composite resins

Abstract

Aim: To investigate the influence of different staining beverages on color stability, surface roughness and microhardness of silorane and methacrylate-based composite resins. Materials and methods: Three different composite resins (Filtek Silorane, Filtek P60, Filtek Supreme XT) were tested. Thirty cylindrical specimens (10 × 2 mm) per material were prepared and polished with a series of aluminum-oxide polishing disks. Each group was then randomly subdivided into three groups according to the test beverages: distilled water (control), cola and coffee. The samples were immersed into different beverages for 15 days. Color, surface roughness and microhardness values were measured by a spectrophotometer, prophylometer and Vickers hardness device respectively, at baseline and after 15 days. The data were subjected to statistical analysis. Results: Immersion in coffee resulted in a significant discoloration for all the composites tested, although the color change was lower in Filtek Silorane than that of MBCs (p < 0.05). All the composites tested showed similar surface roughness changes after immersion in different beverages (p > 0.05). Besides coffee caused more roughness change than others. Immersion in coffee caused highest microhardness change in Filtek Supreme XT (p < 0.05). Conclusion: Cola and coffee altered, to some degree, the color, surface roughness and/or microhardness of the tested resin composites, depending on the characteristics of the materials.